| Mechanical Composition : |
MECHANICAL PROPERTIES |
|||||
Grade |
Tensile |
Yield |
%Age |
Hardness (Max) |
|
BHN |
Rb |
||||
301 |
515 |
205 |
40 |
217 |
95 |
304 |
515 |
205 |
40 |
201 |
92 |
304L |
485 |
170 |
40 |
201 |
92 |
310S |
515 |
205 |
40 |
217 |
95 |
316 |
515 |
205 |
40 |
217 |
95 |
316L |
485 |
170 |
40 |
217 |
95 |
317 |
515 |
205 |
35 |
217 |
95 |
317L |
515 |
205 |
40 |
217 |
95 |
321 |
515 |
205 |
40 |
217 |
95 |
347 |
515 |
205 |
40 |
201 |
92 |
409 |
380 |
170 |
20 |
179 |
88 |
409M |
430 |
275 |
20 |
187 |
90 |
410S |
415 |
205 |
22 |
183 |
89 |
410 |
450 |
205 |
20 |
217 |
89 |
420 |
700( max ) |
- |
15 |
217 |
95 |
430 |
450 |
205 |
22 |
183 |
89 |
JSL AUS |
515 |
205 |
40 |
217 |
95 |
JS- 203 |
515 |
205 |
40 |
217 |
95 |
301M |
515 |
205 |
40 |
217 |
95 |
| Property | Minimum Value (S.I.) | Maximum Value (S.I.) | Units (S.I.) | Minimum Value (Imp.) | Maximum Value (Imp.) | Units (Imp.) |
| Atomic Volume (average) | 0.0065 | 0.0067 | m3/kmol | 396.654 | 408.859 | in3/kmol |
| Density | 8.83 | 8.95 | Mg/m3 | 551.239 | 558.731 | lb/ft3 |
| Energy Content | 230 | 690 | MJ/kg | 24917.9 | 74753.7 | kcal/lb |
| Bulk Modulus | 162 | 200 | GPa | 23.4961 | 29.0075 | 106 psi |
| Compressive Strength | 70 | 935 | MPa | 10.1526 | 135.61 | ksi |
| Ductility | 0.02 | 0.6 | 0.02 | 0.6 | ||
| Elastic Limit | 70 | 935 | MPa | 10.1526 | 135.61 | ksi |
| Endurance Limit | 135 | 500 | MPa | 19.5801 | 72.5188 | ksi |
| Fracture Toughness | 100 | 150 | MPa.m1/2 | 91.0047 | 136.507 | ksi.in1/2 |
| Hardness | 800 | 3000 | MPa | 116.03 | 435.113 | ksi |
| Loss Coefficient | 0.0002 | 0.0032 | 0.0002 | 0.0032 | ||
| Modulus of Rupture | 70 | 935 | MPa | 10.1526 | 135.61 | ksi |
| Poisson's Ratio | 0.305 | 0.315 | 0.305 | 0.315 | ||
| Shear Modulus | 72 | 86 | GPa | 10.4427 | 12.4732 | 106 psi |
| Tensile Strength | 345 | 1000 | MPa | 50.038 | 145.038 | ksi |
| Young's Modulus | 190 | 220 | GPa | 27.5572 | 31.9083 | 106 psi |
| Glass Temperature | K | °F | ||||
| Latent Heat of Fusion | 280 | 310 | kJ/kg | 120.378 | 133.275 | BTU/lb |
| Maximum Service Temperature | 510 | 640 | K | 458.33 | 692.33 | °F |
| Melting Point | 1708 | 1739 | K | 2614.73 | 2670.53 | °F |
| Minimum Service Temperature | 0 | 0 | K | -459.67 | -459.67 | °F |
| Specific Heat | 452 | 460 | J/kg.K | 0.349784 | 0.355975 | BTU/lb.F |
| Thermal Conductivity | 67 | 91 | W/m.K | 125.426 | 170.355 | BTU.ft/h.ft2.F |
| Thermal Expansion | 12 | 13.5 | 10-6/K | 21.6 | 24.3 | 10-6/°F |
| Breakdown Potential | MV/m | V/mil | ||||
| Dielectric Constant | ||||||
| Resistivity | 8 | 10 | 10-8 ohm.m | 8 | 10 | 10-8 ohm.m |